詳細情報 |
|||
| 合金: | 6082 | 気性: | T6 |
|---|---|---|---|
| 直径範囲: | 10mm～350mm | 長さ: | 1000 mm - 6000 mm またはカスタム |
| 形: | 丸棒 | 表面仕上げ: | ミル仕上げ / ポリッシュ |
| 密度: | 2.70 g/cm³ | 抗張力: | ≧310MPa |
| 降伏強さ: | ≧260MPa | 伸長: | ≥10％ |
| 硬度: | 95 HB（標準） | 応用: | 橋梁建設、構造工学、重荷重機械 |
| ハイライト: | 6082 T6 Structural Aluminum Bar,High Strength Engineering Round Rod,Bridge Construction Aluminum Round Bar |
||
製品の説明
6082 T6 High Strength Structural Engineering Round Aluminum Bar Rod For Bridge Construction Heavy Load Applications
Product Overview
6082 T6 round aluminum bar is a medium-to-high strength structural alloy engineered for demanding applications including bridge construction, heavy load machinery, and industrial framework systems. The T6 heat treatment condition delivers optimal mechanical properties with excellent machinability and good corrosion resistance.
Key Features
- High Structural Strength: Tensile strength ≥ 310 MPa, suitable for load-bearing applications
- Excellent Machinability: Consistent chip formation and good surface finish during CNC processing
- Good Corrosion Resistance: Performs reliably in outdoor and industrial environments
- Superior Weldability: Compatible with MIG and TIG welding processes
- Dimensional Stability: Controlled extrusion process ensures tight tolerances
Technical Specifications
| Item | Specification |
|---|---|
| Alloy | 6082 |
| Temper | T6 |
| Diameter Range | 10 mm - 350 mm |
| Length | 1000 mm - 6000 mm or Custom |
| Standard | ASTM B221 / EN 755 |
| Tensile Strength | ≥ 310 MPa |
| Yield Strength | ≥ 260 MPa |
| Hardness | 95 HB Typical |
Applications
- Bridge structural components and support beams
- Heavy load machinery and industrial equipment frames
- Transport and railway engineering structures
- Crane and lifting equipment components
- Construction scaffolding and support systems
6082 vs 6061: Which to Choose?
6082 T6 offers approximately 10-15% higher strength than 6061 T6 while maintaining comparable corrosion resistance. For structural applications requiring maximum load-bearing capacity, 6082 is the preferred engineering alloy.
Frequently Asked Questions
Q: Is 6082 stronger than 6061?
A: Yes, 6082 T6 provides higher tensile and yield strength compared to 6061 T6, making it better suited for structural engineering.
Q: Can 6082 aluminum bars be welded?
A: Yes, 6082 has good weldability with both MIG and TIG processes.
Q: What diameters are available?
A: We supply diameters from 10 mm to 350 mm. Custom sizes are available upon request.
Q: Is surface treatment available?
A: Yes, we offer mill finish, polished, and anodized surface options.